General
Property | Temperature | Value |
---|---|---|
Density |
20.0 °C |
21.6 g/cm³ Show Material materials with Density of 21.6 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus |
20.0 °C |
220 GPa Show Material materials with Elastic modulus of 220 GPa |
|
Elongation |
20.0 °C |
25 % Show Material materials with Elongation of 25 % |
|
Hardness, Vickers |
20.0 °C |
105 [-] Show Material materials with Hardness, Vickers of 105 [-] |
|
Poisson's ratio |
23.0 °C |
0.39 [-] Show Material materials with Poisson's ratio of 0.39 [-] |
Typical for Platinum |
Shear modulus |
23.0 °C |
62 GPa Show Material materials with Shear modulus of 62 GPa |
Typical for Platinum |
Tensile strength |
20.0 °C |
340 MPa Show Material materials with Tensile strength of 340 MPa |
|
Yield strength |
20.0 °C |
220 MPa Show Material materials with Yield strength of 220 MPa |
|
Yield strength Rp0.2 |
20.0 °C |
220 MPa Show Material materials with Yield strength Rp0.2 of 220 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion |
23.0 °C |
8.8E-6 - 9.1E-6 1/K Show Material materials with Coefficient of thermal expansion of 8.8E-6 - 9.1E-6 1/K |
Typical for Platinum |
Melting point |
1769 °C Show Material materials with Melting point of 1769 °C |
Typical for Platinum |
|
Specific heat capacity |
23.0 °C |
136 J/(kg·K) Show Material materials with Specific heat capacity of 136 J/(kg·K) |
Typical for Platinum |
Thermal conductivity |
20.0 °C |
29 W/(m·K) Show Material materials with Thermal conductivity of 29 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical conductivity |
20.0 °C |
4.50E+6 S/m Show Material materials with Electrical conductivity of 4.50E+6 S/m |
Electrical resistivity |
20.0 °C |
2.22E-7 Ω·m Show Material materials with Electrical resistivity of 2.22E-7 Ω·m |